[1]孙成,韦博鑫,覃清钰,等.X80埋地管道应力腐蚀开裂关键影响因素研究进展[J].油气储运,2021,40(09):973-979.[doi:10.6047/j.issn.1000-8241.2021.09.002]
 SUN Cheng,WEI Boxin,QIN Qingyu,et al.Progress of research on key influencing factors of stress corrosion cracking of X80 buried pipeline[J].Oil & Gas Storage and Transportation,2021,40(09):973-979.[doi:10.6047/j.issn.1000-8241.2021.09.002]
点击复制

X80埋地管道应力腐蚀开裂关键影响因素研究进展

参考文献/References:

[1] 冯耀荣,吉玲康,李为卫,刘迎来,霍春勇. 中国X80 管线钢和钢管研发应用进展及展望[J]. 油气储运,2020,39(6):612-622.
FENG Y R,JI L K,LI W W,LIU Y L,HUO C Y. Progress and prospects of research and application of X80 pipeline steel and steel pipe in China[J]. Oil & Gas Storage and Transportation,2020,39(6):612-622.
[2] 张小强,侯宇,蒋庆梅,冯伟. 中俄东线直径1 422 mm X80 钢级冷弯管设计参数的确定[J]. 油气储运,2020,39(2):222-225.
ZHANG X Q,HOU Y,JIANG Q M,FENG W. Determination of the design parameters of X80 cold bending pipe with 1 422 mm diameter in China-Russia Eastern Gas Pipeline[J]. Oil & Gas Storage and Transportation,2020,39(2):222-225.
[3] WANG Y C,XU L Y,SUN J L,CHENG Y F. Mechanoelectrochemical interaction for pipeline corrosion:a review[J]. Journal of Pipeline Science and Engineering,2021,1(1):1-16.
[4] CAZENAVE P,JIMENEZ K,GAO M,MONETA A,HRYCIUK P. Hydrogen assisted cracking driven by cathodic protection operated at near -1 200 mV CSE - an onshore natural gas pipeline failure[J]. Journal of Pipeline Science and Engineering,2021,1(1):100-121.
[5] KIM C,CHEN L,WANG H,CASTANEDA H. Global and local parameters for characterizing and modeling external corrosion in underground coated steel pipelines:a review of critical factors[J]. Journal of Pipeline Science and Engineering,2021,1(1):17-35.
[6] 马晓凤,李媛媛,赵凯峰,刘彬,王晨,吕祥鸿. 埋地管道防腐保温层下的电化学腐蚀行为[J]. 西安石油大学学报(自然科学版),2021,36(3):105-112
MA X F,LI Y Y,ZHAO K F,LIU B,WANG C,LYU X H. Electrochemical corrosion behavior of buried pipeline under anticorrosion and thermal insulation layer[J]. Journal of Xi'an Shiyou University (Natural Science Edition),2021,36(3):105-112.
[7] 谢俊,高长征,单晓琨,李炳辰. CO2-H2S 对X65 钢腐蚀行为研究[J]. 石油规划设计,2020,31(4):13-17.
XIE J,GAO C Z,SHAN X K,LI B C. Study on CO2-H2S corrosion behavior and mechanism of X65 Steel[J]. Petroleum Planning & Engineering,2020,31(4):13-17.
[8] NIAZI H,WANG S D,LAMBORN L,EADIE R,CHEN W X,ZHANG H. Effects of load interactions on the onset of stage two of high pH stress corrosion cracking[J]. Journal of Pipeline Science and Engineering,2021,1(1):122-136.
[9] 蔡亮,姚森,李建国,李磊,郝小虎. 长输管道交流干扰腐蚀判定准则探讨[J]. 石油工业技术监督,2020,36(7):30-33.
CAI L,YAO S,LI J G,LI L,HAO X H. Discussion on criterion for AC interference corrosion of long distance pipeline[J]. Technology Supervision in Petroleum Industry,2020,36(7):30-33.
[10] 刘广鑫,吴明,谢飞,宫克. HCO3-对X100 管线钢在海洋环境中电化学腐蚀行为影响[J]. 石油化工高等学校学报,2019,32(2):66-70.
LIU G X,WU M,XIE F,GONG K. Effect of HCO3- on electrochemical corrosion behavior of X100 pipeline steel in marine environment[J]. Journal of Petrochemical Universities,2019,32(2):66-70.
[11] 许进,白云龙,徐大可,杜翠薇,孙成. 土壤环境中管线钢硫酸盐还原菌腐蚀[J]. 表面技术,2019,48(7):263-270.
XU J,BAI Y L,XU D K,DU C W,SUN C. Sulfate reducing bacteria influenced corrosion of pipeline steel in soil[J]. Surface Technology,2019,48(7):263-270.
[12] 程玉峰. 保障中俄东线天然气管道长期安全运行的若干技术思考[J]. 油气储运,2020,39(1):1-8.
CHENG Y F. Technical insights into the long-term integrity and sustainability of China-Russia Eastern Gas Pipeline[J]. Oil & Gas Storage and Transportation,2020,39(1):1-8.
[13] JIA Y Z,WANG J Q,HAN E H,KE W. Stress corrosion cracking of X80 pipeline steel in near-neutral pH environment under constant load tests with and without preload[J]. Journal of Materials Science & Technology,2011,27(11):1039-1046.
[14] LIANG P,DU C W,LI X G,CHEN X,LIANG Z. Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution[J]. InternationalJournal of Minerals,Metallurgy and Materials,2009,16(4):407-413.
[15] WEI B X,XU J,FU Q,QIN Q Y,BAI Y L,SUN C,et al. Effect of sulfate-reducing bacteria on corrosion of X80 pipeline steel under disbonded coating in a red soil solution[J]. Journal of Materials Science & Technology,2021,87:1-17.
[16] FU Q,XU J,WEI B X,QIN Q Y,GAP L Q,BAI Y L,et al. The effect of nitrate reducing bacteria on the corrosion behavior of X80 pipeline steel in the soil extract solution of Shenyang[J]. International Journal of Pressure Vessels and Piping,2021,190:104313.
[17] 刘相局,黄彦良. 微生物作用下碳钢阴极保护氢渗透研究方法[J]. 装备环境工程,2018,15(10):72-76.
LIU X J,HUANG Y L. Investigation methods for hydrogen permeation of carbon steel with cathodic protection in presence of microorganisms[J]. Equipment Environmental Engineering,2018,15(10):72-76.
[18] 陈士强,张盾. 管线钢的海水微生物腐蚀[J]. 装备环境工程,2018,15(10):39-44.
CHEN S Q,ZHANG D. Microbiologically influenced corrosion of pipeline steel in seawater[J]. Equipment Environmental Engineering,2018,15(10):39-44.
[19] 韦博鑫,许进,高立群,覃清钰,付琦,于长坤,等. 油气管线钢土壤环境硫酸盐还原菌腐蚀研究进展[J]. 表面技术,2021,50(3):30-44.
WEI B X,XU J,GAO L Q,QIN Q Y,FU Q,YU C K,et al. Research progress on sulfate reducing bacteria induced corrosion of pipeline steel in soil environment[J]. Surface Technology,2021,50(3):30-44.
[20] WANG D,XIE F,WU M,LIU G X,ZONG Y,LI X. Stress corrosion cracking behavior of X80 pipeline steel in acid soil environment with SRB[J]. Metallurgical and Materials Transactions A,2017,48(6):2999-3007.
[21] 万红霞,李婷婷,宋东东,陈长风. X80 管线钢在硫酸盐还原菌作用下的腐蚀行为[J]. 表面技术,2020,49(9):281-290.
WAN H X,LI T T,SONG D D,CHEN C F. Effect of SRB on corrosion behavior of X80 pipeline steel[J]. Surface Technology,2020,49(9):281-290.
[22] WEI B X,QIN Q Y,BAI Y L,YU C K,XU J,SUN C,et al. Short-period corrosion of X80 pipeline steel induced by AC current in acidic red soil[J]. Engineering Failure Analysis,2019,105:156-175.
[23] 韦博鑫,许进,高立群,台闯,于长坤,孙成,等. 交流杂散电流对X80 管线钢的腐蚀行为影响[J]. 装备环境工程,2021,18(4):21-27.
WEI B X,XU J,GAO L Q,TAI C,YU C K,SUN C,et al. Effect of AC stray current on corrosion behavior of X80 pipeline steel[J]. Equipment Environmental Engineering,2021,18(4):21-27.
[24] LIU Z Y,LI Q,CUI Z Y,WU W,LI Z,DU C W,et al. Field experiment of stress corrosion cracking behavior of high strength pipeline steels in typical soil environments[J]. Construction and Building Materials,2017,148:131-139.
[25] NIAZI H,EADIE R,CHEN W X,ZHANG H. High pH stress corrosion cracking initiation and crack evolution in buried steel pipelines:a review[J]. Engineering Failure Analysis,2021,120:105013.
[26] CHENG Y F. Stress corrosion cracking of pipelines[M]. New York:John Wiley & Sons,Inc.,2013:117-118.
[27] RYAKHOVSKIKH I V,BOGDANOV R I,IGNATENKO V E. Intergranular stress corrosion cracking of steel gas pipelines in weak alkaline soil electrolytes[J]. Engineering Failure Analysis,2018,94:87-95.
[28] PILKEY A K,LAMBERT S B,PLUMTREE A. Stress corrosion cracking of X-60 line pipe steel in a carbonatebicarbonate solution[J]. Corrosion,1995,51(2):91-96.
[29] SONG F M. Predicting the mechanisms and crack growth rates of pipelines undergoing stress corrosion cracking at high pH[J]. Corrosion Science,2009,51(11):2657-2674.
[30] FRAGIEL A,SERNA S,MALO-TAMAYO J,SILVA P,CAMPILLO B,MARTÍNEZ-MARTÍNEZ E,et al. Effect of microstructure and temperature on the stress corrosion cracking of two microalloyed pipeline steels in H2S environment for gas transport[J]. Engineering Failure Analysis,2019,105:
1055-1068.
[31] WAN H X,SONG D D,LIU Z Y,DU C W,ZENG Z P,YANG X J,et al. Effect of alternating current on stress corrosion cracking behavior and mechanism of X80 pipeline steel in near-neutral solution[J]. Journal of Natural Gas Science and Engineering,2017,38:458-465.
[32] ZHU M,DU C W,LI X G,LIU Z Y,LI H,ZHANG D W. Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution[J]. Corrosion Science,2014,87:224-232.
[33] XU J,BAI Y L,WU T Q,YAN M C,YU C K,SUN C. Effect of elastic stress and alternating current on corrosion of X80 pipeline steel in simulated soil solution[J]. Engineering Failure Analysis,2019,100:192-205.
[34] 王正泉,徐玮辰,周子扬,杨黎晖,李言涛. X65 管线钢在成品油管道沉积物中的微生物腐蚀行为[J]. 表面技术,2020,49(7):245-254.
WANG Z Q,XU W C,ZHOU Z Y,YANG L H,LI Y T. Microbial corrosion behavior of X65 pipeline steel in product pipeline sediments[J]. Surface Technology,2020,49(7):245-254.
[35] ABEDI S S,ABDOLMALEKI A,ADIBI N. Failure analysis of SCC and SRB induced cracking of a transmission oil products pipeline[J]. Engineering Failure Analysis,2007,14(1):250-261.
[36] 刘宏伟,陈翠颖,张雨轩,李伟华. 油气田微生物腐蚀与防护研究进展[J]. 装备环境工程,2020,17(11):1-9.
LIU H W,CHEN C Y,ZHANG Y X,LI W H. Research progress of microbial corrosion and protection in oil and gas fields[J]. Equipment Environmental Engineering,2020,17(11):1-9.
[37] 何奕,杜翠薇,徐大可,张达威,刘智勇. 土壤中的微生物腐蚀研究进展[J]. 装备环境工程,2019,16(3):111-115.
HE Y,DU C W,XU D K,ZHANG D W,LIU Z Y. Research progress on microbiologically influenced corrosion in soil[J]. Equipment Environmental Engineering,2019,16(3):111-115.
[38] WILMOTT M J,JACK T R,VAN BOVEN G,SUTHERBY R. Pipeline stress corrosion cracking:crack growth sensitivity studies under simulated field conditions[C]. Denver:Corrosion 96,1996:NACE-96242.
[39] KHOLODENKO V P,JIGLETSOVA S K,CHUGUNOV V A,RODIN V B,KOBELEV V S,KARPOV S V. Chemicomicrobiological diagnostics of stress corrosion cracking of trunk pipelines[J]. Applied Biochemistry and Microbiology,2000,36(6):594-601.
[40] WU T Q,YAN M C,ZENG D C,XU J,SUN C,YU C K,et al. Stress corrosion cracking of X80 steel in the presence of sulfate-reducing bacteria[J]. Journal of Materials Science & Technology,2015,31(4):413-422.
[41] WU T Q,YAN M C,XU J,LIU Y X,SUN C,KE W. Mechano-chemical effect of pipeline steel in microbiological corrosion[J]. Corrosion Science,2016,108:160-168.
[42] WU T Q,XU J,YAN M C,SUN C,YU C K,KE W. Synergistic effect of sulfate-reducing bacteria and elastic stress on corrosion of X80 steel in soil solution[J]. Corrosion Science,2014,83:38-47.
[43] 吴堂清,周昭芬,王鑫铭,张德闯,闫茂成,许进,等. 弹塑性应力作用下X80 管线钢的菌致开裂行为[J]. 表面技术,2019,48(7):285-295.
WU T Q,ZHOU Z F,WANG X M,ZHANG D C,YAN M C,XU J,et al. Bacteria assisted cracking of X80 pipeline steel under the actions of elastic and plastic stresses[J]. Surface Technology,2019,48(7):285-295.
[44] 李琳,刘孟哲,王一丁. 管道参比电位动态跟踪阴极保护装置的研发[J]. 西安石油大学学报(自然科学版),2021,36(1):80-84.
LI L,LIU M Z,WANG Y D. Development of pipeline cathodic protection device by dynamic tracking of reference potential[J]. Journal of Xi'an Shiyou University (Natural Science Edition),2021,36(1):80-84.
[45] 周好斌,袁旺,毛志高,朱名昭,龙雄云,奚运涛. 阴极保护技术在集输管道内壁应用的失效原因及对策[J]. 西安石油大学学报(自然科学版),2020,35(4):97-101.
ZHOU H B,YUAN W,MAO Z G,ZHU M Z,LONG X Y,XI Y T. Analysis of reasons for failure of application of cathodic protection technology in the inner wall protectoin of gathering pipeline and its countermeasures[J]. Journal of Xi'an Shiyou University (Natural Science Edition),2020,35(4):97-101.
[46] 申毅,王荣,任国琪,邓志龙. X80 管线钢在近中性环境中阴极保护下的应力腐蚀敏感性[J]. 材料保护,2015,48(5):42-45,52.
SHEN Y,WANG R,REN G Q,DENG Z L. Stress corrosion susceptibility of X80 pipeline steel under cathodic protection in near neutral environment[J]. Journal of Materials Protection,2015,48(5):42-45,52.

相似文献/References:

[1]富阳,李泳泉,李智梁,等.LPG储罐硫化物应力腐蚀的检测[J].油气储运,2010,29(2):141.[doi:10.6047/j.issn.1000-8241.2010.02.017]
 Fu Yang,Li Yongquan,Li Zhiliang.Detectlon of sulfide-stress Corrosion of LPG Tanks[J].Oil & Gas Storage and Transportation,2010,29(09):141.[doi:10.6047/j.issn.1000-8241.2010.02.017]
[2]赵新伟,张广利,张良,等.外加电位对X80管线钢近中性pH土壤应力腐蚀开裂行为的影响[J].油气储运,2014,33(11):1152.[doi:10.6047/j.issn.1000-8241.2014.11.002]
 ZHAO Xinwei,ZHANG Guangli,ZHANG Liang,et al.Influence of applied potential on stress corrosion cracking behavior of X80 pipeline steel in near-neutral pH soil environments[J].Oil & Gas Storage and Transportation,2014,33(09):1152.[doi:10.6047/j.issn.1000-8241.2014.11.002]
[3]曹永利 姚登樽 苏鑫 周延 于憬.X80 管线钢管体缺陷极限承载能力研究[J].油气储运,2017,36(预出版):1.
 CAO Yongli,YAO Dengzun,SU Xin,et al.Study on the ultimate bearing capacity of defects in X80 pipeline steel[J].Oil & Gas Storage and Transportation,2017,36(09):1.
[4]刘艳,屈定荣,伯士成,等.L245 管线钢硫化氢腐蚀模拟试验[J].油气储运,2018,37(7):804.[doi:10.6047/j.issn.1000-8241.2018.07.013]
 LIU Yan,QU Dingrong,BAI Shicheng,et al.Simulation experiment on the corrosion of L245 pipeline steel in hydrogen sulfide environment[J].Oil & Gas Storage and Transportation,2018,37(09):804.[doi:10.6047/j.issn.1000-8241.2018.07.013]
[5]吴志平 陈振华 戴联双 胡亚博 毕武喜.油气管道腐蚀检测技术发展现状与思考[J].油气储运,2020,39(08):851.[doi:10.6047/j.issn.1000-8241.2020.08.002]
 WU Zhiping,CHEN Zhenhua,DAI Lianshuang,et al.Development status and thinking of oil and gas pipeline corrosion detection technology[J].Oil & Gas Storage and Transportation,2020,39(09):851.[doi:10.6047/j.issn.1000-8241.2020.08.002]

备注/Memo

收稿日期:2021-07-24;修回日期:2021-08-12;编辑:张腾
基金项目:国家自然科学基金资助项目“交流电、阴极极化和微生物多因素作用下剥离涂层内X80 管线钢应力腐蚀机理研究”,51871228;国家自然科学基金资助项目“交流杂散电流和微生物耦合作用下X80 管线钢应力腐蚀机理研究”,51771213;国家自然科学基金资助项目“土壤中硫酸盐还原菌对高强度管线钢应力腐蚀作用机理研究”,51471176。
作者简介:孙成,男,1965 年生,研究员,博士生导师,2004 年博士毕业于中国科学院研究生院材料学专业,现主要从事管道腐蚀与防护技术的研究工作。地址:辽宁省沈阳市沈河区文萃路62 号,110016。电话:13609891782。Email:chengsun@imr.ac.cn

更新日期/Last Update: 2021-09-25