[1]李鹤 封辉 杨坤 池强 马秋荣 霍春勇.断口分离对X90 焊管断裂阻力影响试验[J].油气储运,2019,38(10):1104-1108.[doi:10.6047/j.issn.1000-8241.2019.10.004]
 LI He,FENG Hui,YANG Kun,et al.Test on the effect of fracture separation on the fracture resistance of X90 welded pipe[J].Oil & Gas Storage and Transportation,2019,38(10):1104-1108.[doi:10.6047/j.issn.1000-8241.2019.10.004]
点击复制

断口分离对X90 焊管断裂阻力影响试验

参考文献/References:

[1] MAKINO H,TAKEUCHI I,HIGUCHI R. Fracture propagation and arrest in high-pressure gas transmission pipeline by ultra high strength line pipes[C]. Calgary:ASME International Pipeline Conference,2008:IPC2008-64078.
[2] 李丽锋,罗金恒,赵新伟,等. 管径1422 mm、X80 管道的风险水 平[J]. 油气储运,2016,35(12):1285-1289. LI L F,LUO J H,ZHAO X W,et al. Risk level of OD 1 422 mm X80 pipelines[J]. Oil & Gas Storage and Transportation,2016, 35(12):1285-1289.
[3] 黄少波,胡强,杨眉,等. 焊接热输入对X90 管线钢焊接接头组 织与性能的影响[J]. 金属热处理,2017,42(1):55-59. HUANG S B,HU Q,YANG M,et al. Effect of welding heat input on microstructure and properties of X90 pipeline steel welded joint[J]. Heat Treatment of Metals,2017,42(1):55-59.
[4] 赵新伟,池强,张伟卫,等. 管径1 422 mm 的X80 焊管断裂韧性 指标[J]. 油气储运,2017,36(1):37-43. ZHAO X W,CHI Q,ZHANG W W,et al. Fracture toughness indicators of OD 1 422 mm X80 welded steel pipe[J]. Oil & Gas Storage and Transportation,2017,36(1):37-43.
[5] 李鹤林,吉玲康. 西气东输二线高强韧焊管及保障管道安全运 行的关键技术[J]. 世界钢铁,2009,9(1):56-64. LI H L,JI L K. High strength and ductility welded pipe and key technologies assuring service security for the 2nd West-East Gas Pipeline Project[J]. World Iron & Steel,2009,9(1):56-64.
[6] 熊庆人,冯耀荣,霍春勇,等. X70 管线钢的断口分离现象分析 研究[J]. 机械工程材料,2005,29(12):21-25. XIONG Q R,FENG Y R,HUO C Y,et al. The fracture separation of X70 pipeline steel[J]. Materials for Mechanical Engineering,2005,29(12):21-25.
[7] 饶添荣,李杰. X80 管线钢DWTT 试验断口分离原因分析[J]. 上海金属,2011,33(6):54-56. RAO T R,LI J. Analysis to fracture separation of DWTT tested X80 pipe line steel[J]. Shanghai Metals,2011,33(6):54-56.
[8] 李洋,林冠发,吉玲康,等. 退火对热轧X80 管线钢织构和断口 分离的影响[J]. 机械工程材料,2010,34(10):14-18. LI Y,LIN G F,JI L K,et al. Effect of annealing on texture and fracture separation of rolled X80 pipeline steel[J]. Materials for Mechanical Engineering,2010,34(10):14-18.
[9] 张振永,孟献强,孙学军,等. 中俄东线站场工艺管道用高钢级 低温钢管韧性指标[J]. 油气储运,2018,37(4):435-442. ZHANG Z Y,MENG X Q,SUN X J,et al. Toughness index of low-temperature pipe of high steel grade used for the process pipelines at the station of China-Russia Eastern Natural Gas Pipeline[J]. Oil & Gas Storage and Transportation,2018,37(4):435-442.
[10] 冯耀荣,霍春勇,吉玲康,等. 我国高钢级管线钢和钢管应用基 础研究进展及展望[J]. 石油科学通报,2016,1(1):143-153. FENG Y R,HUO C Y,JI L K,et al. Progress and prospects of research and applications of high grade pipeline steels & steel pipes in China[J]. Petroleum Science Bulletin,2016,1(1):143-153.
[11] LI Y,MENG L,LIN G F,et al. EBSD analysis of fracture separation in X80 line pipe steel[C]. Chicago:Pressure Vessels Piping Conference,2008:PVP2008-61689.
[12] 李鹤,王海涛,黄呈帅,等. 高钢级管线焊管全尺寸气体爆破试 验研究[J]. 压力容器,2013,30(8):21-26,20. LI H,WANG H T,HUANG C S,et al. Full-scale burst test studies for high grade pipeline weld pipe[J]. Pressure Vessel Technology,2013,30(8):21-26,20.
[13] PYSHMINTSEV I Y,LOBANOVA T P,ARABEY A B, et al. Crack arrestability and mechanical properties of 1420mm X80 Grade pipes designed for 11.8 MPa operation pressure[C]. Ostend:Pipeline Technology Conference,2009: Ostend2009-078.
[14] ERDELEN-PEPPLER M,HILLENBRAND H G,KNAUF G. Limits of existing crack arrest models[C]. Ostend:Pipeline Technology Conference,2009:Ostend2009-116.
[15] 方伟,邹斌,李为卫,等. K65(X80)管线钢断口分离及其对冲 击韧性的影响[J]. 焊管,2018,41(2):65-68. FANG W,ZOU B,LI W W,et al. Separations and their contribution into the impact toughness of pipeline steels of strength class K65(X80)[J]. Welded Pipe and Tube,2018, 41(2):65-68.
[16] HARA T,FUJISHIRO T. Effect of separation on ductile crack propagation behavior during drop weight tear test[C]. Maui: International Offshore and Polar Engineering Conference,2011: 237-242.
[17] RUGGIERI C,HIPPERT E. Delamination effects on fracture behavior of a pipeline steel:a numerical investigation of 3-D crack front fields and constraint[J]. International Journal of Pressure Vessels and Piping,2015,128:18-35.
[18] 李家鼎,麻庆申,姜中行,等. 高级别管线钢中几种常见带状组 织浅析[J]. 轧钢,2009,26(6):16-21. LI J D,MA Q S,JIANG Z H,et al. Research on several often occurred band structures of high grade pipeline steel[J]. Steel Rolling,2009,26(6):16-21.
[19] 杨政,任斌,赵新伟,等. 铁素体管线钢的分层裂纹及其对断裂 的影响[J]. 材料研究学报,2007,21(3):311-318. YANG Z,REN B,ZHAO X W,et al. The delamination crack in ferrite pipeline steel and the effect on the fracture[J]. Chinese Journal of Materials Research,2007,21(3):311-318.
[20] 杨政,郭万林,董蕙茹,等. V 型缺口冲击试样缺口根部三维弹 性应力场分析[J]. 焊管,2002,25(6):15-18. YANG Z,GUO W L,DONG H R,et al. Three-dimensional elastic stress fields near V notches of the impact test sample[J]. Welded Pipe and Tube,2002,25(6):15-18.

相似文献/References:

[1]李鹤 封辉 杨坤 池强 马秋荣 霍春勇.断口分离对X90焊管断裂阻力影响试验[J].油气储运,2019,38(07):1.
 LI He,FENG Hui,YANG Kun,et al.Test on the effect of fracture separation on the fracture resistance of X90 welded pipe[J].Oil & Gas Storage and Transportation,2019,38(10):1.

备注/Memo

基金项目:中国石油天然气集团公司科学研究与技术开发项目“十三· 五”课题“高钢级管道失效控制技术”,2016B-3002;中国陕西省自然科学基础研究计划项目“基于组织控制的X80 钢级焊管延性断裂止裂研究”,2011JQ6017。
作者简介:李鹤,男,1978 年生,高级工程师,2009 年博士毕业于东北大学材料学专业,现主要从事输气管道结构完整性技术的研究工作。地址:陕西省西安市锦业二路89 号,710077。电话:029-81887851。Email:lihe008@cnpc.com.cn
编辑:李在蓉

更新日期/Last Update: 2019-10-25