Influence of applied potential on stress corrosion cracking behavior of X80 pipeline steel in near-neutral pH soil environments

References

[1]WENK R L. Field investigation of stress corrosion cracking//Fifth Symposium on Line Pipe Research[C]. Falls Church:Pipeline Research Council International,1974:No. L30174e.

[2]BEAVERS John A. On the mechanism of stress corrosion cracking of natural gas pipeline//Eighth Symposium on Line Pipe Research[C]. Falls Church:Pipeline Research Council International,1993:No. 51680e.

[3]National Energy Board. Stress corrosion cracking on Canadian oil and gas pipelines,Report of the inquiry MH-2-95[R]. Calgary:National Energy Board,1996.

[4]PARKINS R N. Environment sensitive cracking of high-pressure pipelines in contact with carbon dioxide-containing solution,AGA NG-18 report 205[R]. Washington D C:American Gas Association,1992.

[5]Canadian Energy Pipeline Association. Submission to the national energy board,Proceeding MH-2-95 Vol. 2 Appendix D:8-9[Z]. Calgary:Canadian Energy Pipeline Association,1996.

[6]PARKINS R N. Overview of intergranular stress corrosion cracking research activities,AGA PRCI Repoet PR-232-9401 [R]. Washington D C:American Gas Association,1994.

[7]郭浩,李光福,蔡珣,等. X70 管线钢在不同温度近中性 pH 溶液中的应力腐蚀破裂行为[J].金属学报, 2004, 40 (3) : 967-971.

 GUO H,LI G F,CAI X,et al. Stress corrosion cracking behavior of X70 pipeline steel in near-neutral pH solutions at different temperatures[J]. Acta Metallurgica Sinica, 2004, 40 (3):967-971.

[8]GU B,YU W Z,LUO J L,et a1. Transgranular stress corrosion cracking o f X-80 and X-52 pipe line steels in dilute aqueous solution with near-neutral pH[J]. Corrosion,1999,55(3):312-319.

[9]方丙炎,王俭秋,朱自勇. 埋地管道在近中性 pH 和高 pH 环境中的应力腐蚀开裂[J].金属学报, 2001, 37 (5) : 453-458.

 FANG B Y,WANG J Q,ZHU Z Y. The stress corrosion cracking of buried pipelines in near-neutral-pH and high-pH solutions[J]. Acta Metallurgica Sinica, 2001, 37 (5):453-458.

[10]陈旭,吴明,何川,等. 外加电位对 X80 钢及其焊缝在库尔勒土壤模拟溶液中 SCC 行为的影响[J]. 金属学报, 2010, 46 (8) :  951-958.

 CHEN X,WU M,HE C,et al. Effect of applied potential on SCC of X80 pipeline steel and its weld joint in Ku'erle soil simulated solution[J]. Acta Metallurgica Sinica, 2010, 46 (8):951-958.

[11]刘智勇,王长朋,杜翠薇,等. 外加电位对 X80 管线钢在鹰潭土壤模拟溶液中应力腐蚀行为影响[J]. 金属学报, 2011, 47 (11) : 1434-1439.

 LIU Z Y,WANG C P,DU C W,et al. Effect of applied potentials on stress corrosion cracking of X80 pipeline steel in simulated Yingtan soil solution[J]. Acta Metallurgica Sinica, 2011, 47 (11):1434-1439.

[12]王炳英,霍立兴,王东坡,等. X80 管线钢在近中性 pH 溶液中的应力腐蚀开裂[J].天津大学学报, 2007, 40 (6) : 757-760.

 WANG B Y,HUO L X,WANG D P,et al. Stress corrosion cracking of X80 pipeline steel in near-neutral pH values solutions[J]. Journal of Tianjin University, 2007, 40 (6):757-760.

[13]郏义征,李辉,胡楠楠,等. 外加阴极电位对 X100 管线钢近中性 pH 值应力腐蚀开裂行为的影响[J]. 四川大学学报 (工程科学版) , 2013, 45 (4) : 186-191.

 JIA Y Z,LI H,HU N N,et al. Effects of applied cathode potential on the behavior of near-neutral pH SCC of X100 pipeline steel[J]. Journal of Sichuan University (Engineering Science Edition), 2013, 45 (4):186-191.

Memo

-

Last Update: 1900-01-01